STUDY OF THE EFFECT OF NEW FIREFIGHTING COMPOSITIONS ON THE THERMAL PROPERTIES OF WOOD PARTICLES
Abstract
The article presents a differential scanning analysis of samples treated with new formulations for fire extinguishers in which endothermic and exothermic processes were not observed. This situation is confirmed by the fact that the thermal properties of impregnated wood particles in the new composition are much more effective than those of others. By the end of the test experiments, it was determined that the loss of mass as a result of thermal effects on the duration of time of wood particles coated with bentonite and existing SiO2 suspensions, with a surface part, can vary greatly compared to untreated wood.
Downloads
References
2. Термический анализ. Ч.1:Методы термичекого анализа. В.И.Ивлев, Н.Е.Фомин, В.А.Юдин [и др.]. -Саранск: Изд-во Мордов. Ун-та 2017. С. 2-4, 14-17.
3. Сабиров Э.Э. Кремний (IV) оксид (аэросил-380) суспензияларининг ёғоч заррачаларининг термик хусусиятига таъсирини баҳолаш // “Фавқулодда вазиятларни олдини олиш ва бартараф этишнинг долзарб муаммолари” мавзусидаги республика илмий-амалий анжуман материаллари тўплами (2021 йил 25 август). ФВВ Академияси – Т.: 2021. 88-96 б.
4. Сабиров Э.Э., Курбанбаев Ш.Э. Кремний (IV) – оксид (аэросил 380) суспензиялари реологияси ва термик хоссалари орасидаги боғлиқликни ўрганиш орқали уларнинг ёнғинларни ўчириш самарадорлигини баҳолаш // Ёнғин ва портлаш хавфсизлиги. – Ташкент, 2020. – №2(2). – С. 207-216 (05.00.00; №28).
5. Сабиров Э.Э., Махкамов Н.Я., Курбанбаев Ш.Э. Бентонит таркибли суспензияларни олиш ва уларнинг ёғочнинг ёнувчанлигига таъсирини ўрганиш // FAN MUHOFAZA XAVFSIZLIK. – Ташкент, 2020. – №2(5). – С. 151-159 (05.00.00; №36).